Chemical characteristics for dry material |
PLG-1 |
PLG-2 |
PLG-3(i) |
content |
min, % |
max, % |
min, % |
max, % |
min, % |
max, % |
SiО₂ |
49,20 |
52,86 |
51,76 |
58,99 |
51,00 |
63,00 |
TiО₂ |
1,33 |
1,39 |
1,54 |
1,68 |
0,70 |
0,90 |
Al₂О₃ |
31,52 |
33,34 |
27,74 |
31,87 |
25,00 |
27,00 |
Fe₂О₃ |
1,35 |
1,50 |
1,55 |
1,89 |
1,10 |
1,70 |
CaО |
0,23 |
0,27 |
0,22 |
0,26 |
0,61 |
0,77 |
MgО |
0,25 |
0,26 |
0,22 |
0,28 |
0,45 |
0,65 |
K₂О |
0,29 |
0,32 |
0,14 |
0,24 |
0,20 |
0,36 |
Na₂O |
0,29 |
0,32 |
0,14 |
0,25 |
0,16 |
0,29 |
Lost after ignition, LoІ |
11,63 |
12,63 |
10,24 |
11,68 |
9,00 |
12,50 |
moisture |
|
24,00 |
|
24,00 |
|
24,00 |
|
|
|
|
|
|
|
Colorimetry 1196°C |
PLG-1 |
PLG-2 |
PLG-3(i) |
indicator name |
min |
max |
min |
max |
min |
max |
L |
82,00 |
88,00 |
84,00 |
92,00 |
78,00 |
88,00 |
a |
0,60 |
4,00 |
1,25 |
5,25 |
0,60 |
4,00 |
b |
9,00 |
12,50 |
12,00 |
13,50 |
9,00 |
12,50 |
|
|
|
|
|
|
|
Mineral composition |
PLG-1 |
PLG-2 |
PLG-3(i) |
indicator name |
min, % |
max, % |
min, % |
max, % |
min, % |
max, % |
kaolinite |
80,00 |
90,00 |
80,00 |
90,00 |
80,00 |
90,00 |
illitte |
0,50 |
2,00 |
0,50 |
2,00 |
0,50 |
2,00 |
quarts |
5,00 |
20,00 |
5,00 |
20,00 |
5,00 |
20,00 |
accessory |
traces |
traces |
traces |
|
|
|
|
|
|
|
Dry bending strength |
PLG-1 |
PLG-2 |
PLG-3(i) |
indicator name |
min |
max |
min |
max |
min |
max |
MРa, burn (1050°C) |
11,00 |
13,00 |
12,00 |
14,00 |
20,00 |
24,00 |
MРa, dry |
3,00 |
3,50 |
3,50 |
4,00 |
1,00 |
3,80 |
|
|
|
|
|
|
|
Water absortion, 1200°C,% |
1,40 |
2,80 |
1,80 |
6,00 |
6,00 |
10,00 |
|
|
|
|
|
|
|
Total shrinkage, % |
PLG-1 |
PLG-2 |
PLG-3(i) |
indicator name |
min, % |
max, % |
min, % |
max, % |
min, % |
max, % |
1050°C |
10,60 |
13,45 |
11,70 |
13,50 |
6,00 |
8,50 |
1200°C |
16,60 |
20,00 |
14,90 |
20,00 |
16,00 |
17,00 |
|
|
|
|
|
|
|
Particle size distribution,% |
PLG-1 |
PLG-2 |
|
|
Residus 160μ |
1,23 |
5,59 |
|
|
<20μ |
100,00 |
98,50 |
|
|
<10μ |
99,20 |
98,50 |
|
|
<5μ |
97,20 |
95,40 |
|
|
<2μ |
91,70 |
87,80 |
|
|
<1μ |
87,9 |
82,8 |
|
|